EOS NickelAlloy HX raw material is a nickel-chromium-iron-molybdenum alloy  characterized by having high strength and oxidation resistance also at elevated temperatures, and is often used up to 1200°C. Therefore its applications can be found in aerospace technology, gas turbine parts, etc.  While the wrought and cast versions of the alloy generally are solution annealed, the laser melted material manufactured of this powder has a high strength and good elongation already in the as-built condition. Solution annealing of the laser sintered material will homogenize the microstructure, relax internal stresses and increase the elongation, while slightly decreasing the strength.

Standard laser processing parameters results in full melting of the entire geometry, typically with 40 μm layer thickness. Parts built from EOS NickelAlloy HX can be heat treated and material properties can be varied within specified range. In both as-built and solution heat treated states the parts can be machined, spark-eroded, welded, micro shot-peened, polished, and coated if required. Unexposed powder can be reused.